FR TEX Carbon 300


TECHNICAL DATA

FR-TEX system Carbon 300 is a unidirectional (UDI) Carbon Fiber High resistance due to its high performance is ideal for reinforcing structures wood, masonry and reinforced concrete such as beams and slabs.

FIBER PROPERTIES

 

UD

1.80

4150

230

1.8

 

Fiber Orientation (°)

Density (g/cm3)

Tensile strength (MPa)

Elastic modulus (GPa)

Elongation at break (%)

 

COMPOSITE PROPERTIES

 

1.48

50

2110

115

0.61

Density (g/cm3)

Fiber content (%)

Tensile strength (MPa) based on (ASTM D-3039)

Elastic modulus (GPa) based on (ASTM D-3039):

Thickness (mm)

33

EPOXY RESIN

 

Epoxy resin composite of low viscosity and dried at medium temparature and without any solvent.

MECHANICAL PROPERTIES AT 20ºC (after 7 days)

65 ± 5 MPa

05,3 ± 0,2 %

2.200 ± 300 MPa

12,2 ± 1 MPa

 

Tensile strength (PE-10-01-19) based on (ASTM D638M-89)

Elongation at break (PE-10-01-19) based on (ASTM D638M-89)

Elastic modulus (PE-10-01-19) based on (ASTM D638M-89)

Interlaminar adhesion based on (AST36M D1002-72)

CHARACTERISTICS OF LAMINATED ADVANCE COMPOSITE FIBERS

 

The range of ADVANCE COMPOSITE FIBERS laminated products enable different widths due to their lightness in composition and they adapt easily to any shape.

ADVANTAGES OF LAMINATED ADVANCE COMPOSITE FIBERS

· Light material and easy to install.

· Shorter work execution.

· Acceptability of any type of geometry

· No need for maintenance, as there is no risk of corrosion.