FR TEX Carbon 900


TECHNICAL DATA

FR-TEX system Carbon 900 is a unidirectional (UDI) Carbon Fiber module, ideal for control of deflections in reinforced concrete structural elements due to change in load conditions and / or deterioration of the structure. Especially indicated in cases where necessary to significantly increase the bearing capacity of the structure.

FIBER PROPERTIES

 

UD

1.80

4150

230

1.8

 

Fiber Orientation (°)

Density (g/cm3)

Tensile strength (MPa)

Elastic modulus (GPa)

Elongation at break (%)

 

COMPOSITE PROPERTIES

 

1.41

40

1660

103

1.25

Density (g/cm3)

Fiber content (%)

Tensile strength (MPa) based on (ASTM D-3039)

Elastic modulus (GPa) based on (ASTM D-3039):

Thickness (mm)

33

EPOXY RESIN

 

Epoxy resin composite of low viscosity and dried at medium temparature and without any solvent.

MECHANICAL PROPERTIES AT 20ºC (after 7 days)

65 ± 5 MPa

05,3 ± 0,2 %

2.200 ± 300 MPa

12,2 ± 1 MPa

 

Tensile strength (PE-10-01-19) based on (ASTM D638M-89)

Elongation at break (PE-10-01-19) based on (ASTM D638M-89)

Elastic modulus (PE-10-01-19) based on (ASTM D638M-89)

Interlaminar adhesion based on (AST36M D1002-72)

CHARACTERISTICS OF LAMINATED ADVANCE COMPOSITE FIBERS

 

The range of ADVANCE COMPOSITE FIBERS laminated products enable different widths due to their lightness in composition and they adapt easily to any shape.

ADVANTAGES OF LAMINATED ADVANCE COMPOSITE FIBERS

· Light material and easy to install.

· Shorter work execution.

· Acceptability of any type of geometry

· No need for maintenance, as there is no risk of corrosion.