FR TEX Carbon Multiaxial 636


TECHNICAL DATA

The system Multiaxial Carbon FR-TEX fabric 636 is bi-directional fibers high-strength carbon and high modulus, is ideal for
reinforcing structures subjected to shear loads in reinforced concrete and masonry, and knots connection between elements.

FIBER PROPERTIES

 

+45/-45

1.80

4150

230

1.8

 

Fiber Orientation (°)

Density (g/cm3)

Tensile strength (MPa)

Elastic modulus (GPa)

Elongation at break (%)

 

COMPOSITE PROPERTIES

 

1.48

50

350

30

0.70

Density (g/cm3)

Fiber content (%)

Tensile strength (MPa) based on (ASTM D-3039)

Elastic modulus (GPa) based on (ASTM D-3039):

Thickness (mm)

33

EPOXY RESIN

 

Epoxy resin composite of low viscosity and dried at medium temparature and without any solvent.

MECHANICAL PROPERTIES AT 20ºC (after 7 days)

65 ± 5 MPa

05,3 ± 0,2 %

2.200 ± 300 MPa

12,2 ± 1 MPa

 

Tensile strength (PE-10-01-19) based on (ASTM D638M-89)

Elongation at break (PE-10-01-19) based on (ASTM D638M-89)

Elastic modulus (PE-10-01-19) based on (ASTM D638M-89)

Interlaminar adhesion based on (AST36M D1002-72)

CHARACTERISTICS OF LAMINATED ADVANCE COMPOSITE FIBERS

 

The range of ADVANCE COMPOSITE FIBERS laminated products enable different widths due to their lightness in composition and they adapt easily to any shape.

ADVANTAGES OF LAMINATED ADVANCE COMPOSITE FIBERS

· Light material and easy to install.

· Shorter work execution.

· Acceptability of any type of geometry

· No need for maintenance, as there is no risk of corrosion.