FR TEX Glass Multiaxial 936


TECHNICAL DATA

The system Multiaxial Glass FR-TEX 936 is a bidirectional woven glass fibers of high strength, ideal for the reinforcement of
masonry elements such as slabs and steel beams and columns. Also available in fiberglass for reinforcement AR reinforced
concrete structures.

FIBER PROPERTIES

 

45/-45

2.56

1520

73

2.1

 

Fiber Orientation (°)

Density (g/cm3)

Tensile strength (MPa)

Elastic modulus (GPa)

Elongation at break (%)

 

COMPOSITE PROPERTIES

 

1.85

50

120

9

0.73

Density (g/cm3)

Fiber content (%)

Tensile strength (MPa) based on (ASTM D-3039)

Elastic modulus (GPa) based on (ASTM D-3039):

Thickness (mm)

33

EPOXY RESIN

 

Epoxy resin composite of low viscosity and dried at medium temparature and without any solvent.

MECHANICAL PROPERTIES AT 20ºC (after 7 days)

65 ± 5 MPa

05,3 ± 0,2 %

2.200 ± 300 MPa

12,2 ± 1 MPa

 

Tensile strength (PE-10-01-19) based on (ASTM D638M-89)

Elongation at break (PE-10-01-19) based on (ASTM D638M-89)

Elastic modulus (PE-10-01-19) based on (ASTM D638M-89)

Interlaminar adhesion based on (AST36M D1002-72)

CHARACTERISTICS OF LAMINATED ADVANCE COMPOSITE FIBERS

 

The range of ADVANCE COMPOSITE FIBERS laminated products enable different widths due to their lightness in composition and they adapt easily to any shape.

ADVANTAGES OF LAMINATED ADVANCE COMPOSITE FIBERS

· Light material and easy to install.

· Shorter work execution.

· Acceptability of any type of geometry

· No need for maintenance, as there is no risk of corrosion.